フッ化マグネシウム(MgF2)ウェッジウィンドウ
- 30 arcminute Wedge
- Eliminate Etalon Effects and Prevent Cavity Feedback
- Transmission from 200 nm to 6.0 µm
- Custom Options Available
WW61050
Ø1"
Back Reflections from Wedges Are not Collinear with the Incident Beam
(Drawing not to Scale)
WW60530
Ø1/2"
Please Wait
Wedged Window Selection Guide | |
---|---|
Wavelength Range | Substrate Material |
180 nm - 8.0 µm | Calcium Fluoride (CaF2) |
185 nm - 2.1 μm | UV Fused Silica |
200 nm - 5.0 µm | Sapphire |
200 nm - 6.0 µm | Magnesium Fluoride (MgF2) |
200 nm - 11 µm | Barium Fluoride (BaF2) |
250 nm - 1.6 µm | UV Fused Silica for 45° AOI |
350 nm - 2.0 μm | N-BK7 |
600 nm - 16 µm | Zinc Selenide (ZnSe) |
1.2 - 8.0 µm | Silicon (Si) |
2.0 - 16 µm | Germanium (Ge) |
V-Coated Wedged Windows |
特長
- 30 arcminのウェッジウィンドウ
- Ø12.7 mm(1/2インチ)およびØ25.4 mm(1インチ)ウィンドウをご用意
- ARコーティング付きのタイプやカスタム仕様のサイズもご提供可能です。詳細は当社までお問い合わせください。
当社では、コーティング無しのØ12.7 mm(1/2インチ)およびØ25.4 mm(Ø1インチ)フッ化マグネシウム(MgF2)ウェッジウィンドウをご用意しております。ウェッジ付き光学素子はフリンジパターンの発生をなくし、また、面間における共振を防ぐのに役立ちます。ウィンドウはレーザ出力を外部の影響から保護でき、また、ビームサンプリングの用途で使用する際に便利です。 様々な基板材料やコーティングの平面ウィンドウもご用意しております。
MgF2ウィンドウは深紫外線の用途や、さらには真空紫外線の用途にも適しています。120 nmで50%以上の透過率を達成し、エキシマレーザーシステムと一緒に用いる用途や、121 nmの水素ライマンα線を使用する用途に適しています。当社のMgF2 ウィンドウは、紫外線A(UVA)、紫外線B(UVB)、可視および赤外線(IR)領域でも使用でき、200~1000 nmにおいて約94%の透過率、1~6 µmにおいて約95%の透過率を達成します。複屈折を最小限に抑えるため、当社のMgF2 ウィンドウは、結晶軸が光軸に平行になるようにカットされています。
こちらでご紹介しているMgF2ウェッジウィンドウの他に、異なる基板材料を使用したウェッジウィンドウもご用意しております(右のセレクションガイドをご参照ください)。また、一般的なレーザ波長域に対応したARコーティングを施したウェッジ付きレーザーウィンドウや、片面のみ広帯域ARコーティングを施したウェッジ付きビームサンプラもございます。 当社の標準的なARコーティングや、カスタム仕様のサイズ、厚さ、ウェッジ角にも対応可能です。詳細は当社までお問い合わせください。
Posted Comments: | |
No Comments Posted |
Window Selection Guide (Table Sorted by Wavelength) | |||||
---|---|---|---|---|---|
Substrate and Window Type | Wavelength Range | Available AR Coatings | Reflectance over AR Coating Rangea | Transmission Data | Reflectance Data |
Calcium Fluoride (CaF2): Flat or Wedged | 180 nm - 8.0 μm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
UV Fused Silica: Flat, Wedged, V-Coated Flat, or V-Coated Wedged | 185 nm - 2.1 μm | Uncoated (Flat or Wedged) | - | Raw Data | - |
-UV Coating, 245 - 400 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C3 Coating, 261 - 266 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C6 Coating, 350 - 450 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-A Coating, 350 - 700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-B Coating, 650 - 1050 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C Coating, 1050 - 1700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
Sapphire: Flat or Wedged | 200 nm - 5.0 μm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0% at 0° AOI | Raw Data | Raw Data | ||
-E1 Coating, 2.0 - 5.0 µm | Ravg < 1.50%, Rabs < 3.0% (per Surface, 2.0 - 5.0 µm); Ravg < 1.75% (per Surface, 2.0 - 4.0 µm) at 0° AOI | Raw Data | Raw Data | ||
Magnesium Fluoride (MgF2): Flat or Wedged | 200 nm - 6.0 μm | Uncoated | - | Raw Data | - |
Barium Fluoride (BaF2): Flat or Wedged | 200 nm - 11 µm | Uncoated (Wedged Only) | - | Raw Data | - |
-E1 Coating, 2 - 5 µm | Ravg < 1.25%; Rabs < 2.5% at 0° AOI | Raw Data | Raw Data | ||
UV Fused Silica, for 45° AOI: Flat or Wedged | 250 nm - 1.6 µm | Coating for 250 nm - 450 nm | Ravg < 1.0% at 45° AOI | Raw Data | |
Coating for 350 nm - 1100 nm | Ravg < 2.0% at 45° AOI | Raw Data | |||
Coating for 400 nm - 700 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Coating for 600 nm - 1700 nm | Ravg < 1.5% at 45° AOI | Raw Data | |||
Coating for 700 nm - 1100 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Coating for 1200 nm - 1600 nm | Ravg < 1.0% at 45° AOI | Raw Data | |||
Potassium Bromide (KBr): Flat | 250 nm - 26 µm | Uncoated | - | - | |
Infrasil®: Flat | 300 nm - 3 µm | Uncoated | - | Raw Data | - |
N-BK7: Flat, Wedged, V-Coated Flat, or V-Coated Wedged | 350 nm - 2.0 μm | Uncoated (Flat or Wedged) | - | Raw Data | - |
-A Coating, 350 - 700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C7 Coating, 400 - 700 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C10 Coating, 523 - 532 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C11 Coating, 610 - 860 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-B Coating, 650 - 1050 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C13 Coating, 700 - 1100 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
C14 Coating, 1047 - 1064 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C15 Coating, 523 - 532 nm & 1047 - 1064 nm (V-Coated) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
-C Coating, 1050 - 1700 nm (Flat or Wedged) | Ravg < 0.5% at 0° AOI | - | Raw Data | ||
Zinc Selenide (ZnSe): Flat or Wedged | 600 nm - 16 µm | Uncoated | - | Raw Data | - |
-D Coating, 1.65 - 3.0 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-E4 Coating, 2 - 13 µm (Only Flat) | Ravg < 3.5%; Rabs < 6% at 0° AOI | Raw Data | Raw Data | ||
-E2 Coating, 4.5 - 7.5 µm (Only Flat) | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-E3 Coating, 7 - 12 µm (Only Wedged) | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data | ||
-G Coating, 7 - 12 µm (Only Flat) | Ravg < 1% at 0° AOI | Raw Data | Raw Data | ||
Silicon (Si): Flat or Wedged | 1.2 - 8.0 μm | Uncoated | - | Raw Data | - |
-E1 Coating, 2 - 5 µm (Only Wedged) | Ravg < 1.25%; Rabs < 2.5% at 0° AOI | Raw Data | Raw Data | ||
-E Coating, 3 - 5 µm (Only Flat) | Ravg < 2% at 0° AOI | Raw Data | Raw Data | ||
Germanium (Ge): Flat or Wedged | 1.9 - 16 μm | Uncoated, 2.0 - 16 μm | - | Raw Data | - |
-C9 Coating, 1.9 - 6 µm (Only Flat) | Ravg < 2% at 0° AOI | Raw Data | Raw Data | ||
-E3 Coating, 7 - 12 µm | Ravg < 1.0%; Rabs < 2.0% at 0° AOI | Raw Data | Raw Data |
Item # | WW60530 | WW61050 |
---|---|---|
Wedge Angle | 30 ± 10 arcmin | |
Diameter | 1/2" (12.7 mm) | 1" (25.4 mm) |
Diameter Tolerance | +0.0 / -0.2 mm | |
Thickness | 3.0 mm | 5.0 mm |
Thickness Tolerance | ±0.1 mm | |
Clear Aperture | ≥11.43 mm | ≥Ø22.86 mm |
Surface Flatnessa | ≤λ/16 Over Central Ø5 mm ≤λ/8 Over Entire Clear Aperture | ≤λ/16 Over Central Ø10 mm ≤λ/8 Over Entire Clear Aperture |
Surface Quality | 20-10 Scratch-Dig | |
Wavelength Range | 200 nm - 6.0 µm (Uncoated) | |
Substrate | Magnesium Fluorideb | |
Transmission Data (Click for Graph) | Raw Data |